08-03-2018, 08:39 PM
"...but rather considering how universally valid the obtained results are, and to what extend they may reflect some specific properties of the A2 steel."
Mr. Jan, I would be interested in your views on the above.
Mr. KG noted, "The same with hardness - though the initial rolling/blunting rate is rapid regardless of the steel hardness, the higher is HRC, the longer the blade stays work sharp."
There has been so much data posted here in different posts, I don't remember seeing that data. Mr. KG, if you have the supporting data handy could you please repost it?
All this data is now sprinkled throughout various threads and posts. I sure would be handy if all the various data was at least in one place!
Mr. Jan, I would be interested in your views on the above.
Mr. KG noted, "The same with hardness - though the initial rolling/blunting rate is rapid regardless of the steel hardness, the higher is HRC, the longer the blade stays work sharp."
There has been so much data posted here in different posts, I don't remember seeing that data. Mr. KG, if you have the supporting data handy could you please repost it?
All this data is now sprinkled throughout various threads and posts. I sure would be handy if all the various data was at least in one place!