Huh. Are you saying that if you freeze a blade with burrs the blade shatters, but if the edge is clean it does not? i wonder why that happens. Interesting.
My original thinking was that because cold steel is more brittle, it might make deburring easier. I was thinking that you could just direct a fine blast of cold right at the edge as it was deburred. Kind of like coolant in milling operations, only a super cold stream.
My original thinking was that because cold steel is more brittle, it might make deburring easier. I was thinking that you could just direct a fine blast of cold right at the edge as it was deburred. Kind of like coolant in milling operations, only a super cold stream.